Home > Products > Polyurea Waterproofing > UMS-AUPT Polyurea System > T109 Polyurea Waterproof Middle Coating
T109 Polyurea Waterproof Middle Coating
  • T109 Polyurea Waterproof Middle Coating

T109 Polyurea Waterproof Middle Coating

    Payment Type: L/C,T/T,Western Union
    Incoterm: FOB,CIF
    Min. Order: 800 Kilometer
    Delivery Time: 12 Days
Contact Now

Basic Info

Model No.: T109

Special Services: Construction Technical Guidance

Additional Info

Packaging:  Component A: 20KG/barrel Component B: 10KG/barrel

Productivity: 1000000KG/month

Brand: UMSN

Transportation: Ocean,Land

Place of Origin: GUANGNDONG

Supply Ability: 100000KG/month

Certificate: ISO9001

HS Code: 3209100000

Port: XIAMEN,GUANGZHOU,SHENZHEN

Product Description

T109 Polyurea Waterproof Middle Coating

Product introduction Polyaspartic Polyurea

The component A is composed of an aliphatic polyurea resin, a pigment filler, an auxiliary agent and a small amount of an environmentally friendly solvent, and the component B is composed of an aliphatic isocyanate and a prepolymer. Can be hand brushed, this coating and high pressure airless spray. Polyaspartic vs Polyurea


Performance characteristics Polyaspartic Coating

High elongation, high tensile strength, strong adhesion to concrete and good wear resistance. Applicable to the middle layer of indoor floor and floor protection paint, low odor. Also used in the basement, kitchen and bathroom, Waterproof Roof.


Technical Performance

Quick Information
Adhesion
≥ 3.0MPa (or substrate broken)
Density (film)
1.1-1.3g/cm³
Tensile Strength
10MPa
Solid Content (%)
≥90-95%
Elongation at Break
50%
Construction Period(25℃)
50-60min
Tear Strength
≥70kN/m
Dry Film Thickness
600-1000µm
Hardness (Shore A)
≥80
Theoretical Coverage
0.8kg/m² (when dry film is 600µm)
Low Temperature Bending
-35℃
Surface Drying
1h
Wear Resistance (750g/500r)
≤0.03g
Actual Drying
24h


Re-coat Time
3-48h


Construction Methods
Brush, roller, airless spraying, spraying


Mixing: waterproof coating: curing agent = 2:1 (please see label notice)


Shelf Life: Polyurea A component for 12 months

Curing agent component B for 6 months (products are qualified for inspection, can still be used)

Package: Polyurea Coating 20kg Curing agent 10kg


Polyaspartic Coatings, We offer a mini sample kit and a money back guarantee.



Looking for ideal T109 Waterproof Coating Manufacturer & supplier ? We have a wide selection at great prices to help you get creative. All the T109 Polyurea Coating are quality guaranteed. We are China Origin Factory of Waterproof Middle Coating. If you have any question, please feel free to contact us.

Product Categories : Polyurea Waterproofing > UMS-AUPT Polyurea System

Email to this supplier
  • Mr. Thomas Tang
  • Your message must be between 20-8000 characters

Related Products List

Home

Phone

Skype

Inquiry